Ultrason® E 2010 UN Q26
聚醚砜
BASF Corporation
Technical Data
產品說明
Unreinforced, medium viscosity standard injection moulding grade. Abbreviated designation according to ISO 1043-1: PESU
Physical form and storage:
Ultrason® pellets are supplied in bags and/or octabins. The bulk density ranges between 700 and 800 g/l. Provided the packaging remains undamaged, Ultrason® can be stored indefinitely. Ultrason® pellets absorb moisture very rapidly. Therefore, the pellets need to be dried at least 4h at 130 °C to 150 °C in a vacuum or dry air drier prior to processing.
總體
材料狀態 • 已商用：當前有效
資料 1 • Technical Datasheet (English)
Search for UL Yellow Card • BASF Corporation
• Ultrason® E
供貨地區 • 歐洲
性能特點 • 中等粘性
機構評級 • EC 1907/2006 (REACH)
RoHS 合規性 • RoHS 合規
形式 • 顆粒料
加工方法 • 注射成型
部件標識代碼 • PESU
樹脂ID (ISO 1043) • PESU
物理性能 額定值單位制 測試方法
密度 1.37g/cm³ ISO 1183
溶化體積流率（MVR） (360°C/10.0 kg) 70.0cm³/10min ISO 1133
收縮率 3 ISO 294-4
橫向流量: 23°C 0.86%
流量: 23°C 0.82%
吸水率 ISO 62
飽和, 23°C 2.2%
平衡, 23°C, 50% RH 0.80%
粘數 4 56.0cm³/g ISO 307
機械性能 額定值單位制 測試方法
拉伸模量 (23°C) 27000MPa ISO 527-2
拉伸應力 (屈服, 23°C) 90.0MPa ISO 527-2/50
拉伸應變 (屈服, 23°C) 6.7% ISO 527-2/50
沖擊性能 額定值單位制 測試方法
簡支梁缺口沖擊強度 (23°C) 6.5kJ/m² ISO 179/1eA
簡支梁缺口沖擊強度 (23°C) 無斷裂 ISO 179/1eU
懸壁梁缺口沖擊強度 (23°C) 6.5kJ/m² ISO 180/A
硬度 額定值單位制 測試方法
球壓硬度 (H 358/30) 154MPa ISO 2039-1
熱性能 額定值單位制 測試方法
熱變形溫度 (1.8 MPa, 未退火) 205°C ISO 75-2/A
玻璃轉化溫度(DSC) 5 225°C ISO 11357-2
線形膨脹系數 - 流動
23 到 80°C 0.000052cm/cm/°C ISO 11359-2
180°C 0.000059cm/cm/°C DIN 53752
可燃性 額定值單位制 測試方法
UL 阻燃等級 (1.60 mm) V-0 UL 94
1 / 3
Ultrason® E 2010 UN Q26
聚醚砜
BASF Corporation
注射 額定值單位制
干燥溫度 130 到 150°C
干燥時間 4.0hr
加工（熔體）溫度 340 到 390°C
模具溫度 140 到 180°C
擠出 額定值單位制
熔體溫度 340 到 390°C
備注
1 通過這些鏈接您能夠訪問供應商資料。我們盡量保證及時更新資料；不過您可以從供應商處了解最新資料。
2 一般屬性：這些不能被視為規格。
3 ISO 2577
4 in 0,01 g/ml Phenol/1,2, ortho-Dichlorbenzol, 1:1
5 10°C/min
|