G-Blend 85 PC/ABS
丙烯腈丁二烯苯乙烯+聚碳酸酯
Gardiner Compounds Ltd.
Technical Data
產品說明
G-Blend 65/85/85HI is a non-reinforced, amorphous thermoplastic polymer blend based on polycarbonate and acrylonitrile butadiene styrene. It is noted for its toughness, rigidity and ability to flow and mould easily.
This blend contains a proportion of recycled and prime material to produce a polymer that offers outstanding properties, giving users the benefit of considerable cost down over equivalent prime grades.
G-Blend 65/85/85HI complies with all the recycling directives and can be recycled in the normal way.
Typical applications include interior automotive trim, mobile phone housings, electrical and electronic enclosures and some household goods. This material is available in a black and natural and a whole range of colours.
總體
材料狀態 • 已商用：當前有效
資料 1 • Technical Datasheet (English)
供貨地區 • 歐洲
回收含量 • 是
性能特點 • 非晶性 • 良好的成型性能 • 韌性良好
• 剛性，高 • 良好的流動性
用途 • Electrical Housing • 家用貨品 • 汽車外部裝飾
• 電氣/電子應用領域 • 汽車內部裝備 • 手機
外觀 • 黑色 • 自然色
加工方法 • 注射成型
物理性能 額定值單位制 測試方法
密度 1.15g/cm³ ISO 1183
熔流率 (260°C/5.0 kg) 15g/10 min ISO 1133
收縮率 3 0.50 到 0.70% ISO 2577
吸水率 (平衡, 23°C, 85%RH) 0.20% ISO 62
機械性能 額定值單位制 測試方法
拉伸模量 2200MPa ISO 527-2/1
拉伸應力 (斷裂) 53.0MPa ISO 527-2/50
拉伸應變 (屈服) 5.0% ISO 527-2/50
沖擊性能 額定值單位制 測試方法
懸壁梁缺口沖擊強度 (23°C) 60kJ/m² ISO 180/1A
無缺口伊佐德沖擊強度 (23°C) 無斷裂 ISO 180/1U
熱性能 額定值單位制 測試方法
熱變形溫度 (1.8 MPa, 未退火) 110°C ISO 75-2/A
維卡軟化溫度 130°C ISO 306/B120
可燃性 額定值單位制 測試方法
UL 阻燃等級 (1.60 mm) HB UL 94
注射 額定值單位制
干燥溫度 90.0 到 110°C
干燥時間 2.0 到 4.0hr
建議的最大水分含量 < 0.020%
螺筒后部溫度 240 到 260°C
螺筒中部溫度 245 到 265°C
螺筒前部溫度 250 到 270°C
射嘴溫度 240 到 260°C
加工（熔體）溫度 280°C
模具溫度 70.0 到 100°C
1 / 3
G-Blend 85 PC/ABS
丙烯腈丁二烯苯乙烯+聚碳酸酯
Gardiner Compounds Ltd.
注射說明
Max Dwell Time: 8 mins
備注
1 通過這些鏈接您能夠訪問供應商資料。我們盡量保證及時更新資料；不過您可以從供應商處了解最新資料。
2 一般屬性：這些不能被視為規格。
3 500 bar
|